Shear Bond Strength of Acrylic Denture Teeth to Different Pmma/Mgo % Reinforcing Nanofillers
DOI:
https://doi.org/10.32828/mdj.v17i1.1013Keywords:
MgO nanofiller particles, heat cure acrylic resin (PMMA), shear bond strength (B.S).Abstract
Aim of the study: The objective of this study was to evaluate the shear bond strength of acrylic denture teeth to different PMMA/MgO % (2%, 4%, and 6%) reinforcing nanofillers
Materials and method: 40 specimens of heat cure acrylic resin (PMMA) were prepared and divided into four groups 10 specimens for each group as follows; Control Group (Group1) without MgO nano filler particles; Group (2) with 2% by weight of MgO; Group (3) with 4% by weight of MgO and Group (4) with 6% by weight of MgO. Wax pattern sample which used for acrylic cylindrical shape fabrication were (25 mm in length and 5mm in diameter, the base of the cylinder which is 5mm in thickness and 8mm in length). Shear bond strength of all specimens was evaluated.
Results: Showed in the PMMA+MgO 4% showed the maximum mean value of upper bound of shear bond strength which was equaled to (14.859) while the control group PMMA recorded the minimum value of lower bound of shear bond strength (8.190).
Conclusion: There was no significant difference between control group PMMA and (PMMA+MgO 2%, PMMA+MgO 6%), but there was a significant difference between PMMA+Mgo4% compared with control group PMMA.
References
-American dental association specification No. 12 (1983) for denture base polymers. Chicago.: Council on dental materials and devices.
-Craig RG; Power JM (2002): "Restorative dental material" llthedition. ST. Louis: Mosby, p.50, 185-195.
-Manappallil JJ.: "Basic dental material”. 2ndedition, JAYPEE brothers. Medical publisher, New Delhi (2007); p 100-142.
-McCabe J.F. and Walls A.W.G.: “Applied dental material”, 9th edition. Black well scientific publication, London (2008). ch. l3, p110-123.
-Rohm and Haas Innovation – Plexiglas Triumphs. Rohmhaas.com. 2010.
-Schomover, I.C., Fischer, T.E., Serio, A.F., and Sweeny, A.B (Bonding of plastic teeth to heat cure acrylic denture base) JAM Dent Assoc,1952, P44-285.
-Mohamed, R., Noufal, P., Shenoy, D., Reddy, P. S., Varma, A., & Jain, A. R. (2017). A Comparitive Study on the Tensile Bond Strength of Conventional Denture Base Resin to Cross Linked Acrylic Tooth using two Different Curing Cycles–an invitro Study. Biomedical and Pharmacology Journal, 10(1), 447-454.
-Liu G, Li YF, Yan FY, Zhao ZX, Zhou LC, Xue QJ. Effect of nanoscale SiO2 and TiO2 as the fillers on the mechanical properties and aging behavior of linear low-density polyethylene/ low-density polyethylene blends. J Polym Environ 2005; 13:339-48.
-(AZoNano, 2013) Magnesium Oxide (MgO) Nanoparticles - Properties, Applications.
-Vatsha, B., Tetyana, P., Shumbula, P. M., Ngila, J. C., Sikhwivhilu, L. M., & Moutloali, R. M. (2013). Effects of precipitation temperature on nanoparticle surface area and antibacterial behaviour of Mg (OH) 2 and MgO nanoparticles. Journal of Biomaterials and Nanobiotechnology, 4(04), 365.
-(Corrosionpedia ,2013) Shear Strength, Definition - What does Shear Strength mean.
-Abu- Anzeh M. L (2003): Evaluation of tensile bond strength of tooth-denture base resin as a function at different surface treatment and processing regimes .M.Sc . Thesis. College of Dentistry, University of Baghdad.
-Al-Huwaizi, A. F. (2005). An evaluation of the effect of retention means on increasing the debonding strength of the denture acrylic teeth attached to the denture base resin. Journal of baghdad college of dentistry, 17(1), 14-17.
-Yaseen, I. N. (2016). Effect of different surface treatments on the tensile bond strength between acrylic resin teeth and denture base material. Iraqi Dental Journal, 38(3), 142-146.
-Aljudy, H. J., Hussein, A. N., & Safi, I. N. (2013). Effect of surface treatments and thermocycling on shear bond strength of various artificial teeth with different denture base materials. Journal of baghdad college of dentistry, 25(1), 5-13.
-Alnamel, H. A., & Mudhaffer, M. (2014). The effect of Silicon di oxide Nano-Fillers reinforcement on some properties of heat cure polymethyl methacrylate denture base material. Journal of baghdad college of dentistry, 26(1), 32-36.
-Craig R.G; John M. Powers; John C.W. “dental material properties and manipulation”, Eight edition, 2004, p.270-280.
-Abduallah, H. A. (2012). Evaluation of Shear Bond Strength of Composite Resin Bonded to Dentin with Three Different Adhesive Systems. Tikrit Journal for Dental Sciences, 1(2), 13-18.
-Sun L.; Ronald F.G.; Suhr J. and Groanine J.F (2009):” Toughening polymeric composites using Nano composite: A review “composite science and technology.
-Hu Y.; Zhou S. and Wu L.:”surface mechanical properties of PMMA /silica Nano composite prepared by in situ bulk polymerization.”polymer,50:p299-304,2009
-Singh D.; J Ayasimha T.; Rai K.N.and Kumar A. (2007):” preparation of PMMA Nano composite with superior impact strength. J.appl. polym.Sci. 105(6): p3183-3194
Downloads
Published
How to Cite
Issue
Section
Categories
License
This work is licensed under a Creative Commons Attribution 4.0 International License.
This work is licensed under a Creative Commons Attribution 4.0 International License.